Oxygen Free High Conductivity Copper (OFHC) - C10100

Atlas carries C10100 Oxygen Free High Conductivity Copper (OFHC) in Sheet / Plate, Rod & Tubing. We carry a very large range of sizes and will cut the material to length.

C10100 OFHC Copper is produced by the direct conversion of selected refined cathodes and castings under carefully controlled conditions to prevent contamination of the pure oxygen-free metal during processing. The method of producing C10100 OFHC copper ensures extra high grade of metal with a copper content of 99.99%. With so small a content of extraneous elements, the inherent properties of elemental copper are brought forth to a high degree.

Characteristics of C10100 Oxygen Free High Conductivity copper are:

  • High Ductility
  • High Electrical & Thermal Conductivity
  • High Impact Strength
  • Good Creep Resistance
  • Ease of Welding
  • Low Relative Volatility under high vacuum

C10100 Copper Sheet Plate RFQ C10100 Copper Sheet Plate RFQ

C10100 Copper Rod RFQ C10100 Copper Rod RFQ

C10100 Copper Tube RFQC10100 Copper Tube RFQ


C10100 OFHC COPPER TYPICAL USES

  • Transistor Component Bases,
  • High Resistance-Ratio Cryogenic Shunts,
  • Bus Conductors,
  • Wave Guides,
  • Hollow Conductors,
  • Anodes for Vacuum Tubes,
  • Coaxial Cable,
  • Coaxial Tube,
  • Klystrons,
  • Microwave Tubes,
  • Bus Bars,
  • Lead-in Wire,
  • Vacuum Seals,
  • Conductors,
  • Glass-to-Metal Seals

C10100 CHEMICAL COMPOSITION

(%max., unless shown as range or min.)
NOTE: Information courtesy copper.org

Cu(1) Sb As O P Te
Min./Max. 99.99 min .0004 .0005 .0005 .0003 .0002
Nominal - - - - - -

(1) Cu is determined by the difference between the impurity total and 100%. The Cu value is exclusive of Ag.
Note: This is a high conductivity copper which has, in the annealed condition a minimum conductivity of 100% IACS except for Alloy C10100 which has a minimum conductivity of 101% IACS.
Note: The following additional impurity maximum limits shall apply: Bi, 1ppm (.0001%); Cd, 1ppm (.0001%); Fe, 10ppm (.0010%); Pb, 5ppm (.0005%); Mn, 0.5ppm (.00005%); Ni, 10ppm (.0010%); Se, 3ppm (.0003%); Ag, 25ppm(.0025%);S, 15ppm (.0015%); Sn, 2ppm (.0002%); Zn, 1ppm (.0001%).

C10100 MECHANICAL PROPERTIES

(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy copper.org

Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Tube
H80 0.065 0 TYP 68 55 50 - - 8 60 - 95 63 - - - 29 - 0.0

1.65

20 379 345 - - 8 60 - 95 63 - - - 200 - 0.0
Flat Products
M20 0.25 0 TYP 68 32 10 - - 50 - - 40 - - - - 22 - 0.0

6.35

20 221 69 - - 50 - - 40 - - - - 152 - 0.0
H04 0.25 0 TYP 68 50 45 - - 12 50 - 90 - - - - 28 - 0.0

6.35

20 345 310 - - 12 50 - 90 - - - - 193 - 0.0
H02 0.04 0 TYP 68 42 36 - - 14 40 - 84 50 - - - 26 13 0.0

1

20 290 248 - - 14 40 - 84 50 - - - 179 90 0.0
Rod
M20 1 0 TYP 68 32 10 - - 55 - - 40 - - - - 22 - 0.0

25.4

20 221 69 - - 55 - - 40 - - - - 152 - 0.0
Flat Products
H04 0.04 0 TYP 68 50 45 - - 6 50 - 90 57 - - - 28 13 0.0

1

20 345 310 - - 6 50 - 90 57 - - - 193 90 0.0
Rod
H04 0.25 40 TYP 68 55 50 - - 10 60 - 94 - - - - 29 - 0.0

6.35

20 379 345 - - 10