C63200 Nickel Aluminum Bronze Forgings


Atlas offers
C63200 Nickel Aluminum Bronze Forgings in Plate, Rounds and Rings per ASTM B124 or ASTM B171.

Forgings have distinct advantages over the other methods of Casting (such as Continuous Cast or Sand Castings). Forgings are not only a cost effective process that yields the optimum in performance, but also offer the flexibility of size change. For instance if it becomes necessary to increase a diameter or thickness, open-die forging readily accommodates such a change.

ADVANTAGES
:

  • Reduces the cross-section
  • Improves the metallurgical microstructure
  • Provide directional grain flow
  • Eliminates porosity in Cast ingot





This is a Made to Order product. Tell us what your desired sizes are and we will work up a quote for you. Please indicate if any specifications that must be met.



__________________________________________________________________________________________



TYPICAL USES:
Some of the typical areas that C63200 is used in, is as follows: Bearing Cages, Sleeve Bearings, Valve Stems, Shafts, Cams, Sea Water Valves, Sea Water Pump Bodies, Bushings



CHEMICAL COMPOSITION:

(%max., unless shown as range or min.)
Cu(1) Al Fe(2) Pb Mn Ni(3) Si
Min./Max. Rem. 8.7-9.5 3.5-4.3 .02 1.2-2.0 4.0-4.8 .10
Nominal 82.0 9.0 4.0 - 1.6 4.4 -

(1) Cu value includes Ag.
(2) Fe content shall not exceed Ni content.
(3) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.


MECHANICAL PROPERTIES:

(measured at room temperature, 68 F (20 C)
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Plate
O50 1 0 TYP 68 90 45 - - 25 85 - - - - - - - - 0.0

25.4

20 621 310 - - 25 85 - - - - - - - - 0.0
Rod
O50 1 0 TYP 68 105 53 - - 22 96 - - - - - - - - 0.0

25.4

20 724 365 - - 22 96 - - - - - - - - 0.0
Plate
O50 0.5 0 TYP 68 95 47 - - 22 89 - - - - - - - - 0.0

12.7

20 655 324 - - 22 89 - - - - - - - - 0.0
O50 0.25 0 TYP 68 100 50 - - 20 92 - - - - - - - - 0.0

6.35

20 689 345 - - 20 92 - - - - - - - - 0.0
Rod
O50 3 0 TYP 68 102 51 - - 24 93 - - - - - - - - 0.0

76

20 703 352 - - 24 93 - - - - - - - - 0.0
O50 2 0 TYP 68 103 52 - - 24 94 - - - - - - - - 0.0

51

20 710 359 - - 24 94 - - - - - - - - 0.0
Forgings
O50 5 0 TYP 68 100 45 - - 22 92 - - - - - - - - 0.0

127

20 689 310 - - 22 92 -