C93500 High Leaded Tin Bronze, SAE 66
Atlas Bronze offers C93500 High Leaded Tin Bronze, SAE 66 in Centrifugal Castings and Sand Castings. This alloy
is not available as an Off-the-Shelf product but as a special castings only. The method in which the material is
cast will depend on your
size, specification and desired quantity.
__________________________________________________________________________________________
TYPICALLY USED FOR:
This
material is used in a variety of applications. Typical uses for this
alloy are: Small bearings and bushings, bronze backing for babbitt-lined automotive bearings.
CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
|
|
Cu(1)
|
Al
|
Sb
|
Fe
|
Pb
|
Ni(2)
|
P(3)
|
Si
|
S
|
Sn
|
Zn
|
|
Min./Max.
|
83.0-86.0
|
.005
|
.30
|
.20
|
8.0-10.0
|
1.0
|
.05
|
.005
|
.08
|
4.3-6.0
|
2.0
|
|
Nominal
|
84.5
|
-
|
-
|
-
|
9.0
|
-
|
-
|
-
|
-
|
5.2
|
-
|
(1) In determining Cu min., Cu may be calculated as Cu + Ni.
(2) Ni value includes Co.
(3) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.0% min.
MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
|
Temper
|
Section
Size
|
Cold
Work
|
Typ/
Min
|
Temp
|
Tensile
Strength
|
Yield
Strength
(0.5% ext.
under load)
|
Yield
Strength
(0.2%
offset)
|
Yield
Strength
(0.05%
offset)
|
El
|
Rockwell
Hardness
|
Vickens
Hard.
|
Brinell
Hard.
|
Shear
Strength
|
Fatigue
Strength*
|
Izod
Impact
Strength
|
|
in.
|
%
|
|
F
|
ksi
|
ksi
|
ksi
|
ksi
|
%
|
B
|
C
|
F
|
30T
|
500
|
500
|
3000
|
ksi
|
ksi
|
ft-lb
|
|
mm.
|
|
|
C
|
MPa
|
MPa
|
MPa
|
MPa
|
|
|
|
|
|
|
|
|
MPa
|
MPa
|
J
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
TYP
|
68
|
32
|
16
|
-
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
60
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
221
|
110
|
-
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
60
|
-
|
-
|
-
|
0.0
|
|
As Centrifugal Cast
|
|
M02
|
0.0
|
0
|
SMIN
|
68
|
28
|
12
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
193
|
83
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Continuous Cast
|
|
M07
|
0.0
|
0
|
SMIN
|
68
|
30
|
16
|
-
|
-
|
12
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
207
|
110
|
-
|
-
|
12
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
SMIN
|
68
|
28
|
12
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
193
|
83
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.
APPLICABLE SPECIFICATIONS:
NOTE: Information courtesy of Copper.org
|
Product
|
Specification
|
|
Centrifugal
|
ASTM B271
SAE J462, J461
|
|
Continuous
|
ASTM B505
SAE J461, J462
|
|
Ingot
|
ASTM B30
|
|
Sand
|
ASTM B584, B763
SAE J461, J462
|
|