C65100 Low Silicon Bronze Solid Bar



Atlas carries C65100 Low Silicon Bronze B Solid Bar stock in full bar lengths and we will cut to you exact lengths per your requirements. We carry a very large range of sizes and will cut the material to length.

__________________________________________________________________________________________






Available in the following sizes:

.2500" diameter - PART# 6510S-2
.3125" diameter - PART# 6510S-2.5
.3310" diameter - PART# 6510S-2.648
.3750" diameter - PART# 6510S-3
.4375" diameter - PART# 6510S-3.5
.4470" diameter - PART# 6510S-3.576
.5000" diameter - PART# 6510S-4
.6250" diameter - PART# 6510S-5
.6810" diameter - PART# 6510S-5.448
.6875" diameter - PART# 6510S-5.5
.7500" diameter - PART# 6510S-6
.8750" diameter - PART# 6510S-7
.9375" diameter - PART# 6510S-7.5
1.000" diameter - PART# 6510S-8
1.125" diameter - PART# 6510S-9
1.1875" diameter - PART# 6510S-9.5
1.2500" diameter - PART# 6510S-10
1.3750" diameter - PART# 6510S-11
1.5000" diameter - PART# 6510S-12
1.6250" diameter - PART# 6510S-13
1.7500" diameter - PART# 6510S-14
1.8750" diameter - PART# 6510S-15
2.0000" diameter - PART# 6510S-16
2.2500" diameter - PART# 6510S-18
2.7500" diameter - PART# 6510S-22
3.0000" diameter - PART# 6510S-24
3.2500" diameter - PART# 6510S-26
3.5000" diameter - PART# 6510S-28
3.7500" diameter - PART# 6510S-30
4.0000" diameter - PART# 6510S-32
4.5000" diameter - PART# 6510S-36
5.0000" diameter - PART# 6510S-40

__________________________________________________________________________________________


TYPICAL USES:
Some of the typical areas that C65100 is used in, is as follows: In aircraft: Hydraulic pressure lines. As hardware: Anchor screws, bolts, cable clamps, cap screws, machine screws, marine hardware, nuts, pole line hardware, rivets, U-bolts



CHEMICAL COMPOSITION:

(%max., unless shown as range or min.)
Cu(1) Fe Pb Mn Si Zn
Min./Max. Rem. .8 .05 .7 .8-2.0 1.5
Nominal 98.5 - - - 1.5 -

(1) Cu value includes Ag.
Note: Cu + Sum of Named Elements, 99.5% min.



MECHANICAL PROPERTIES
:

(measured at room temperature, 68 F (20 C)
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Rod
OS035 1 0 TYP 68 40 15 - - 50 - - 55 - - - - - - 0.0

25.4

20 276 103 - - 50 - - 55 - - - - - - 0.0
Wire
H06 0.08 0 TYP 68 105 71 - - 10 - - - - - - - 53 28 0.0

2

20 724 490 - - 10 - - - - - - - 365 193 0.0
Tube
H80 0.0 35 TYP 68 65 40 - - 20 75 - - 67 - - - - - 0.0

0.0

20 448 276 - - 20 75 - - 67 - - - - - 0.0
Rod
H06 1 50 TYP 68 90 67 - - 12 90 - - - - - - 50 - 0.0

25.4

20 621 462 - - 12 90 - - - - - - 345 - 0.0
Wire
H04 0.44 60 TYP 68 95 - - - 12 - - - - - - - - - 0.0

11

20 655 - - - 12 - - - - - - - - - 0.0
H01 0.08 0 TYP 68 65 50 - - 25 - - - - - - - 40 - 0.0

2

20 448 345 - - 25 - - - - - - - 276 - 0.0
H00 0.08 0 TYP 68 55 40 - - 40 - - - - - - - 36 - 0.0

2

20 379 276 - - 40 - - - - - - - 248 - 0.0
Rod