C63200 Nickel Aluminum Solid Bar
Atlas carries C63200 Nickel Aluminum Bronze Solid Bar, ASTM B150, QQ-C-465, TQ50.
This material is highly suitable for salt water applications due to it's superior corrosion resistance. We stock Solid Bar Stock in this alloy group and also offer Made to Order plate Forgings. We offer full bars and will cut your material to length. Some
of the typical areas that C63200 is used in, is as follows: Bearing
Cages, Sleeve Bearings, Valve Stems, Shafts, Cams, Sea Water Valves, Sea
Water Pump Bodies, Bushings.
ASTM B150 is the specification for rods, bars, and
shapes that covers the alloy C63200 Nickel Aluminum Solid Bar. C63200 products shall be produced in tempers HR50, M10, M20, M30, O20, O25,
O30, O32, TQ30, TQ50 and TQ55. Products shall be tested and shall
conform to dimensional (mass, diameter, length, thickness, straightness,
and edge contour), mechanical (tensile and yield strength, Rockwell
hardness, and elongation), and chemical composition requirements.
__________________________________________________________________________________________
Available in the following sizes:
1.000" diameter - PART# 6320S-8
1.250" diameter - PART# 6320S-10
1.500" diameter - PART# 6320S-12
1.750" diameter - PART# 6320S-14
2.000" diameter - PART# 6320S-16
2.250" diameter - PART# 6320S-18
2.500" diameter - PART# 6320S-20
2.750" diameter - PART# 6320S-22
3.000" diameter - PART# 6320S-24
3.250" diameter - PART# 6320S-26
3.500" diameter - PART# 6320S-28
3.750" diameter - PART# 6320S-30
4.000" diameter - PART# 6320S-32
4.250" diameter - PART# 6320S-34
4.500" diameter - PART# 6320S-36
4.750" diameter - PART# 6320S-38
5.000" diameter - PART# 6320S-40
5.250" diameter - PART# 6320S-42
5.500" diameter - PART# 6320S-44
5.750" diameter - PART# 6320S-46
6.000" diameter - PART# 6320S-48
6.250" diameter - PART# 6320S-50
6.500" diameter - PART# 6320S-52
6.750" diameter - PART# 6320S-54
7.000" diameter - PART# 6320S-56
7.500" diameter - PART# 6320S-60
8.000" diameter - PART# 6320S-64
8.500" diameter - PART# 6320S-68
9.000" diameter - PART# 6320S-72
9.500" diameter - PART# 6320S-76
10.00" diameter - PART# 6320S-80
CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
|
|
Cu(1)
|
Al
|
Fe(2)
|
Pb
|
Mn
|
Ni(3)
|
Si
|
|
Min./Max.
|
Rem.
|
8.7-9.5
|
3.5-4.3
|
.02
|
1.2-2.0
|
4.0-4.8
|
.10
|
|
Nominal
|
82.0
|
9.0
|
4.0
|
-
|
1.6
|
4.4
|
-
|
(1) Cu value includes Ag.
(2) Fe content shall not exceed Ni content.
(3) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.
MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
|
Temper
|
Section
Size
|
Cold
Work
|
Typ/
Min
|
Temp
|
Tensile
Strength
|
Yield
Strength
(0.5% ext.
under load)
|
Yield
Strength
(0.2%
offset)
|
Yield
Strength
(0.05%
offset)
|
El
|
Rockwell
Hardness
|
Vickens
Hard.
|
Brinell
Hard.
|
Shear
Strength
|
Fatigue
Strength*
|
Izod
Impact
Strength
|
|
in.
|
%
|
|
F
|
ksi
|
ksi
|
ksi
|
ksi
|
%
|
B
|
C
|
F
|
30T
|
500
|
500
|
3000
|
ksi
|
ksi
|
ft-lb
|
|
mm.
|
|
|
C
|
MPa
|
MPa
|
MPa
|
MPa
|
|
|
|
|
|
|
|
|
MPa
|
MPa
|
J
|
|
Plate
|
|
O50
|
1
|
0
|
TYP
|
68
|
90
|
45
|
-
|
-
|
25
|
85
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
25.4
|
|
|
20
|
621
|
310
|
-
|
-
|
25
|
85
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
Rod
|
|
O50
|
1
|
0
|
TYP
|
68
|
105
|
53
|
-
|
-
|
22
|
96
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
25.4
|
|
|
20
|
724
|
365
|
-
|
-
|
22
|
96
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
Plate
|
|
O50
|
0.5
|
0
|
TYP
|
68
|
95
|
47
|
-
|
-
|
22
|
89
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
12.7
|
|
|
20
|
655
|
324
|
-
|
-
|
22
|
89
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
O50
|
0.25
|
0
|
TYP
|
68
|
100
|
50
|
-
|
-
|
20
|
92
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
6.35
|
|
|
20
|
689
|
345
|
-
|
-
|
20
|
92
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
Rod
|
|
O50
|
3
|
0
|
TYP
|
68
|
102
|
51
|
-
|
-
|
24
|
93
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
76
|
|
|
20
|
703
|
352
|
-
|
-
|
24
|
93
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
O50
|
2
|
0
|
TYP
|
68
|
103
|
52
|
-
|
-
|
24
|
94
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
51
|
|
|
20
|
710
|
359
|
-
|
-
|
24
|
94
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
Forgings
|
|
O50
|
5
|
0
|
TYP
|
68
|
100
|
45
|
-
|
-
|
22
|
92
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
127
|
|
|
20
|
689
|
310
|
-
|
-
|
22
|
92
|
-
|
|
|