C93700 Solid Bar
C93700 Tin Bronze Solid Bar
Atlas Bronze offers C93700 Tin Bronze Solid Bar stock. Atlas stocks a select variety
of diameters in full bar lengths and we will cut to your desired length.
This
material is used in a variety of applications. Typical uses for this
alloy are: Fasteners: Washers for Engines, Industrial:
Crank Shafts, Bushings, Machine Parts, High Speed, Heavy Load Bearings,
Pumps, Pressure Tight Castings, Impellers, Bushings for high speed and
heavy pressure, Bearings, Bearing Plates, Parts for Steel Mill
Maintenance, Marine: Large Bearings for Ships
__________________________________________________________________________________________
DIAMETER (inches)
| PART NUMBER | | .6250" | 9370S-5 | | 1.000" | 9370S-8 | | 1.125" | 9370S-9 | | 1.250" | 9370S-10 | | 1.375" | 9370S-11 | | 1.500" | 9370S-12 | | 1.625" | 9370S-13 | | 1.750" | 9370S-14 | | 2.000" | 9370S-16 | | 2.500" | 9370S-20 | | 2.625" | 9370S-21 | | 3.000" | 9370S-24 | | 3.500" | 9370S-28 | | 3.625" | 9370S-29 | | 4.000" | 9370S-32 | | 4.500" | 9370S-36 | | 5.250" | 9370S-42 | | 6.000" | 9370S-48 |
__________________________________________________________________________________________
TYPICALLY USED FOR:
This
material is used in a variety of applications. Typical uses for this
alloy are: Fasteners: Washers for Engines, Industrial:
Crank Shafts, Bushings, Machine Parts, High Speed, Heavy Load Bearings,
Pumps, Pressure Tight Castings, Impellers, Bushings for high speed and
heavy pressure., Bearings, Bearing Plates, Parts for Steel Mill
Maintenance, Marine: Large Bearings for Ships
CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
| |
Cu | Al | Sb | Fe(1) | Pb | Ni(2) | P(3) | Si | S | Sn | Zn |
|---|
| Min./Max. | 78.0-82.0 | .005 | .50 | .7 | 8.0-11.0 | .50 | .10 | .005 | .08 | 9.0-11.0 | .8 | | Nominal | 80.0 | - | - | - | 9.5 | - | - | - | - | 10.0 | - |
(1) Fe shall be .35% max., when used for steel-backed
(2) Ni value includes Co.
(3) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.0% min.
MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
| Temper |
Section
Size |
Cold
Work |
Typ/
Min |
Temp |
Tensile
Strength |
Yield
Strength
(0.5% ext.
under load) |
Yield
Strength
(0.2%
offset) |
Yield
Strength
(0.05%
offset) |
El |
Rockwell
Hardness |
Vickens
Hard. |
Brinell
Hard. |
Shear
Strength |
Fatigue
Strength* |
Izod
Impact
Strength |
|---|
| in. |
% |
| F |
ksi |
ksi |
ksi |
ksi |
% |
B |
C |
F |
30T |
500 |
500 |
3000 |
ksi |
ksi |
ft-lb |
| mm. |
|
| C |
MPa |
MPa |
MPa |
MPa |
|
|
|
|
|
|
|
|
MPa |
MPa |
J |
| As Sand Cast | | M01 | 0.0 | 0 | TYP | 68 | 35 | 18 | 16 | - | 20 | - | - | - | - | - | 60 | - | 18 | 13 | 5.0 |
| 0.0 |
|
| 20 | 241 | 124 | 110 | - | 20 | - | - | - | - | - | 60 | - | 124 | 90 | 7.0 | | As Centrifugal Cast | | M02 | 0.0 | 0 | SMIN | 68 | 30 | 12 | - | - | 15 | - | - | - | - | - | - | - | - | - | 0.0 |
| 0.0 |
|
| 20 | 207 | 83 | - | - | 15 | - | - | - | - | - | - | - | - | - | 0.0 | | As Continuous Cast | | M07 | 0.0 | 0 | SMIN | 68 | 35 | 20 | - | - | 6 | - | - | - | - | - | - | - | - | - | 0.0 |
| 0.0 |
|
| 20 | 241 | 138 | - | - | 6 | - | - | - | - | - | - | - | - | - | 0.0 | | As Sand Cast | | M01 | 0.0 | 0 | SMIN | 68 | 30 | 12 | - | - | 15 | - | - | - | - | - | - | - | - | - | 0.0 |
| 0.0 |
|
| 20 | 207 | 83 | - | - | 15 | - | - | - | - | - | - | - | - | - | 0.0 |
*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.
APPLICABLE SPECIFICATIONS:
NOTE: Information courtesy of Copper.org
| Product | Specification |
| Bearings | AMS 4827 | | Centrifugal | AMS 4842
ASTM B271
SAE J462, J461 | | Continuous | ASTM B505
SAE J461, J462 | | Ingot | ASTM B30 | | Sand | AMS 4842
ASME SB584
ASTM B763, B66, B584, B22
SAE J461, J462 |
|