Home > PRODUCT LIST > Bronze Bushings
Our Bronze Bushings are machined from Continuous Cast bar stock. Depending on the type of Bushing selected, they are offered in C93200 Bearing Bronze (SAE 660), C95400 Aluminum Bronze & C86300 Manganese Bronze for superior quality and performance. The continuous casting process assures a uniform bronze structure throughout the bearing, free from porosity and hard particle inclusions commonly found in other cast processes.

Our standard bearing lines feature over 1,000 sizes that are carried in stock. These standards provide off-the-shelf economy for most applications, and may be easily resized, oil grooved, or graphited to meet special requirements.

When quotations are made for Bushings that are "Machined to Print" or "Made from Sample" parts, we welcome drawings in a number of formats, such as; Adobe .pdf, Microsoft Word, Koday .jpeg's and CAD file to meet our customers needs.

__________________________________________________________________________________________


Below you will find the 3 Types of Bushings: Sleeve Bearing, Flange Bearing & Thrust Bearing. Each type is available as a Plain, Oil or Grease Grooved and Graphite Plugged.












__________________________________________________________________________________________


C93200 CHEMICAL COMPOSITION:

(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
Cu(1) Al Sb Fe Pb Ni(2) P(3) Si S Sn Zn
Min./Max. 81.0-85.0 .005 .35 .20 6.0-8.0 1.0 .15 .005 .08 6.3-7.5 1.0-4.0
Nominal 83.0 - - - 7.0 - - - - 6.9 2.5

(1) In determining Cu min., Cu may be calculated as Cu + Ni.
(2) Ni value includes Co.
(3) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.0% min.



C93200 MECHANICAL PROPERTIES:

(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
As Sand Cast
M01 0.0 0 TYP 68 35 18 - - 20 - - - - - 65 - - 16 6.0

0.0

20 241 124 - - 20 - - - - - 65 - - 110 8.0
As Centrifugal Cast
M02 0.0 0 SMIN 68 30 14 - - 15 - - - - - - - - - 0.0

0.0

20 207 97 - - 15 - - - - - - - - - 0.0
As Continuous Cast
M07 0.0 0 SMIN 68 35 20 - - 10 - - - - - - - - - 0.0

0.0

20 241 138 - - 10 - - - - - - - - - 0.0
As Sand Cast
M01 0.0 0 SMIN 68 30 14 - - 15 - - - - - - - - - 0.0

0.0

20 207 97 - - 15 - - - - - - - - - 0.0

*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.



C93200 APPLICABLE SPECIFICATIONS:

NOTE: Information courtesy of Copper.org
Product Specification
Centrifugal ASTM B271
SAE J462, J461
Continuous ASTM B505
SAE J461, J462
Ingot ASTM B30
Permanent Mold SAE J461, J462
Sand ASTM B584, B763, B66
SAE J462, J461