C93600 High Leaded Tin Bronze, MOD SAE 64 Solid Bar

Atlas Bronze offers
C93600 High Leaded Tin Bronze, MOD SAE 64 Solid Bar stock. Atlas stocks CDA 936 solid bar as full bar lengths and we will cut to your exact requirements.

Atlas stocks a select variety of sizes in Rounds and various sizes on a Made to Order basis. Please note that the method in which the material is cast will depend on your
size, specification and desired quantity.

__________________________________________________________________________________________






DIAMETER (inches)PART NUMBER
.5000"9360S-4
.6250"9360S-5
.7500"9360S-6
.8750"9360S-7
1.000"9360S-8
1.125"9360S-9
1.250"9360S-10
1.375"9360S-11
1.500"9360S-12
1.625"9360S-13
1.750"9360S-14
2.000"9360S-16
2.125"9360S-17
2.250"9360S-18
2.500"9360S-20
2.750"9360S-22
3.000"9360S-24
3.500"9360S-28
3.750"9360S-30
4.000"9360S-32
4.250"9360S-34
4.500"9360S-36
4.750"9360S-38
5.000"9360S-40
5.500"9360S-44
6.000"9360S-48
6.500"9360S-52
7.000"9360S-56
8.000"9360S-64
9.000"9360S-72
10.00"9360S-80
11.00"9360S-88
12.00"9360S-96
12.50"9360S-100
_________________________________________________________________________________________



TYPICALLY USED FOR:


This material is used in a variety of applications. Typical uses for this alloy are: Bushings for corrosion, lubrication or pressure, Cam Bushings for Diesel Engines, Crankshaft Main Bearings, Guide Bushings for Piston Rods, Guide Bushings for Valves, Hydraulic Gland Seals, Locomotive Bearing Parts, Main Bearings for Presses, Piston Pin Bearings, Pump Sleeves, Rod Bushings, Rolling Mill Bearings, Sleeve Bushings (for Cranes, etc.), Bearings for corrosion, lubrication or pressure.



CHEMICAL COMPOSITION:

(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
CuAlSbFePbNi(1)P(2)SiSSnZn
Min./Max.79.0-83.0.005.55.2011.0-13.01.0.15.005.086.0-8.01.0
Nominal81.0---12.0----7.0-

(1) Ni value includes Co.
(2) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.3% min.



MECHANICAL PROPERTIES:

(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
As Centrifugal Cast
M020.00TYP683521--15-----65---0.0

0.0

20241145--15-----65---0.0
M020.00SMIN683216--10---------0.0

0.0

20221110--10---------0.0
As Continuous Cast
M070.00SMIN683320--10---------0.0

0.0

20227138--10---------0.0
M070.00TYP683521--15-----65---0.0

0.0

20241145--15-----65---0.0
As Permanent Mold Cast
M050.00TYP683521--15-----65---0.0

0.0

20241145--15-----65---0.0

*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.