C92200 Leaded Tin, Navy M Solid Bar



Atlas Bronze offers C92200 Leaded Tin Bronze, Navy M Solid Bar stock. Atlas Bronze offers CDA 922 Solid Bar per ASTM B505 stock in both full bar length and we will cut the material to your desired length as required.

This material is used in a variety of applications. Typical uses for this alloy are: Valves, fittings, and pressure containing parts for use up to 550°F.

________________________________________________________________________________________







DIAMETER (inches) PART NUMBER
.8750" 9220S-7
1.000"
9220S-8
1.125" 9220S-9
1.250" 9220S-10
1.750" 9220S-14
2.000" 9220S-16
2.500" 9220S-20
2.750" 9220S-22
3.000" 9220S-24
3.500" 9220S-28
4.000" 9220S-32
4.500" 9220S-36
5.000" 9220S-40
5.500" 9220S-44
6.000" 9220S-48
__________________________________________________________________________________________



TYPICALLY USED FOR:


This material is used in a variety of applications. Typical uses for this alloy are: Valves, fittings, and pressure containing parts for use up to 550°F.



CHEMICAL COMPOSITION:

(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
Cu(1) Al Sb Fe Pb Ni(2) P(3) Si S Sn Zn
Min./Max. 86.0-90.0 .005 .25 .25 1.0-2.0 1.0 .05 .005 .05 5.5-6.5 3.0-5.0
Nominal 88.0 - - - 1.5 - - - - 6.0 4.5

(1) In determining Cu min., Cu may be calculated as Cu + Ni.
(2) Ni value includes Co.
(3) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.3% min.



MECHANICAL PROPERTIES:

(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
As Sand Cast
M01 0.0 0 TYP 68 40 20 - - 30 - - - - - 65 - - 11 0.0

0.0

20 276 138 - - 30 - - - - - 65 - - 76 0.0
As Centrifugal Cast
M02 0.0 0 SMIN 68 34 16 - - 22 - - - - - - - - - 0.0

0.0

20 234 110 - - 22 - - - - - - - - - 0.0
As Continuous Cast
M07 0.0 0 SMIN 68 38 19 - - 18 - - - - - - - - - 0.0

0.0

20 262 131 - - 18 - - - - - - - - - 0.0
As Permanent Mold Cast
M05 0.0 0 SMIN 68 34 16 - - 24 - - - - - - - - - 0.0

0.0

20 234 110 - - 24 - - - - - - - - - 0.0
As Sand Cast
M01 0.0 0 SMIN 68 34 16 - - 22 - - - - - - - - - 0.0

0.0

20 234 110 - - 22 - - - - - - - - - 0.0

*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.



APPLICABLE SPECIFICATIONS:

NOTE: Information courtesy of Copper.org
Product Specification
Centrifugal ASTM B271
SAE J462, J461
Continuous ASTM B505
SAE J462, J461
Fittings ASME B16.24, SB61
ASTM B61
FEDERAL WW-P-460
Flanges ASME SB61
ASTM B61
FEDERAL WW-P-460
Ingot ASTM B30
Sand ASME SB61, SB584
ASTM B61, B584
SAE J461, J462
Valves MILITARY MIL-V-17547