C90500 Tin Bronze Solid Bar
Atlas Bronze offers C90500 Tin Bronze, Gun Metal SAE 62 Solid Bar stock. This alloy
is available as both an Off-the-Shelf product and in special castings. The method in which the material is
cast will depend on your
size, specification and desired quantity.
__________________________________________________________________________________________
.5000" diameter - PART# 9050S-4
.6250" diameter - PART# 9050S-5
.7500" diameter - PART# 9050S-6
.9375" diameter - PART# 9050S-7.5
1.000" diameter - PART# 9050S-8
1.250" diameter - PART# 9050S-10
1.500" diameter - PART# 9050S-12
1.750" diameter - PART# 9050S-14
2.000" diameter - PART# 9050S-16
2.250" diameter - PART# 9050S-18
2.500" diameter - PART# 9050S-20
3.000" diameter - PART# 9050S-24
3.500" diameter - PART# 9050S-28
3.750" diameter - PART# 9050S-30
4.000" diameter - PART# 9050S-32
__________________________________________________________________________________________
TYPICALLY USED FOR:
This
material is used in a variety of applications. Typical uses for this
alloy are: Bearings and bushings, pump impellers, valve components, seal rings, steam fittings, gears.
CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
|
|
Cu(1)
|
Al
|
Sb
|
Fe
|
Pb
|
Ni(2)
|
P(3)
|
Si
|
S
|
Sn
|
Zn
|
|
Min./Max.
|
86.0-89.0
|
.005
|
.20
|
.20
|
.30
|
1.0
|
.05
|
.005
|
.05
|
9.0-11.0
|
1.0-3.0
|
|
Nominal
|
87.5
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
10.0
|
2.0
|
(1) In determining Cu min., Cu may be calculated as Cu + Ni.
(2) Ni value includes Co.
(3) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.7% min.
MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
|
Temper
|
Section
Size
|
Cold
Work
|
Typ/
Min
|
Temp
|
Tensile
Strength
|
Yield
Strength
(0.5% ext.
under load)
|
Yield
Strength
(0.2%
offset)
|
Yield
Strength
(0.05%
offset)
|
El
|
Rockwell
Hardness
|
Vickens
Hard.
|
Brinell
Hard.
|
Shear
Strength
|
Fatigue
Strength*
|
Izod
Impact
Strength
|
|
in.
|
%
|
|
F
|
ksi
|
ksi
|
ksi
|
ksi
|
%
|
B
|
C
|
F
|
30T
|
500
|
500
|
3000
|
ksi
|
ksi
|
ft-lb
|
|
mm.
|
|
|
C
|
MPa
|
MPa
|
MPa
|
MPa
|
|
|
|
|
|
|
|
|
MPa
|
MPa
|
J
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
TYP
|
68
|
45
|
22
|
-
|
-
|
25
|
-
|
-
|
-
|
-
|
-
|
75
|
-
|
-
|
13
|
10.0
|
|
0.0
|
|
|
20
|
310
|
152
|
-
|
-
|
25
|
-
|
-
|
-
|
-
|
-
|
75
|
-
|
-
|
90
|
13.0
|
|
As Centrifugal Cast
|
|
M02
|
0.0
|
0
|
TYP
|
68
|
45
|
22
|
-
|
-
|
25
|
-
|
-
|
-
|
-
|
-
|
75
|
-
|
-
|
13
|
10.0
|
|
0.0
|
|
|
20
|
310
|
152
|
-
|
-
|
25
|
-
|
-
|
-
|
-
|
-
|
75
|
-
|
-
|
90
|
13.0
|
|
M02
|
0.0
|
0
|
SMIN
|
68
|
40
|
18
|
-
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
276
|
124
|
-
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Continuous Cast
|
|
M07
|
0.0
|
0
|
SMIN
|
68
|
44
|
25
|
-
|
-
|
10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
303
|
172
|
-
|
-
|
10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
SMIN
|
68
|
40
|
18
|
-
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
275
|
124
|
-
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.
APPLICABLE SPECIFICATIONS:
NOTE: Information courtesy of Copper.org
|
Product
|
Specification
|
|
Centrifugal
|
AMS 4845
ASTM B271
SAE J462, J461
|
|
Continuous
|
ASTM B505
SAE J462, J461
|
|
Ingot
|
ASTM B30
|
|
Sand
|
AMS 4845
ASTM B763, B584, B22
SAE J462, J461
|
CONGRATULATIONS Stephanie Krill - You won!!
Come back tomorrow - same time - 2:00 p.m. EST to play again!
|