Atlas carries C67600 Manganese Bronze in
Solid Bar stock. We carry a very large range of sizes and will cut the
material to length.
__________________________________________________________________________________________
Click on the below image to select your size:
 
__________________________________________________________________________________________
TYPICAL USES:
Some of the typical areas that C67600 is used in, is as follows: Gate Valve Stems, Welding Rod, and Valve Balls
CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
| |
Cu(1) | Fe | Pb | Mn | Sn | Zn |
|---|
| Min./Max. | 57.0-60.0 | .40-1.3 | .50-1.0 | .05-.50 | .50-1.5 | Rem. | | Nominal | 58.5 | .8 | .7 | .27 | 1.0 | 38.7 |
(1) Cu value includes Ag.
Note: Cu + Sum of Named Elements, 99.5% min.
MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
| Temper |
Section
Size |
Cold
Work |
Typ/
Min |
Temp |
Tensile
Strength |
Yield
Strength
(0.5% ext.
under load) |
Yield
Strength
(0.2%
offset) |
Yield
Strength
(0.05%
offset) |
El |
Rockwell
Hardness |
Vickens
Hard. |
Brinell
Hard. |
Shear
Strength |
Fatigue
Strength* |
Izod
Impact
Strength |
|---|
| in. |
% |
| F |
ksi |
ksi |
ksi |
ksi |
% |
B |
C |
F |
30T |
500 |
500 |
3000 |
ksi |
ksi |
ft-lb |
| mm. |
|
| C |
MPa |
MPa |
MPa |
MPa |
|
|
|
|
|
|
|
|
MPa |
MPa |
J |
| Rod | | H01 | 2 | 0 | TYP | 68 | 72 | 42 | - | - | - | 77 | - | - | - | - | - | - | - | - | 0.0 |
| 50.8 |
|
| 20 | 496 | 290 | - | - | - | 77 | - | - | - | - | - | - | - | - | 0.0 | | H02 | 1 | 0 | TYP | 68 | 84 | 60 | - | - | - | 90 | - | - | - | - | - | - | - | - | 0.0 |
| 25.4 |
|
| 20 | 579 | 414 | - | - | - | 90 | - | - | - | - | - | - | - | - | 0.0 | | H02 | 1 | 0 | MIN | 68 | - | - | - | - | 19 | - | - | - | - | - | - | - | - | - | 0.0 |
| 25.4 |
|
| 20 | - | - | - | - | 19 | - | - | - | - | - | - | - | - | - | 0.0 | | H01 | 2 | 0 | MIN | 68 | - | - | - | - | 27 | - | - | - | - | - | - | - | - | - | 0.0 |
| 50.8 |
|
| 20 | - | - | - | - | 27 | - | - | - | - | - | - | - | - | - | 0.0 | | H01 | 1 | 0 | MIN | 68 | - | - | - | - | 23 | - | - | - | - | - | - | - | - | - | 0.0 |
| 25.4 |
|
| 20 | - | - | - | - | 23 | - | - | - | - | - | - | - | - | - | 0.0 | | O60 | 0.0 | 0 | TYP | 68 | 65 | 30 | - | - | - | 65 | - | - | - | - | - | - | - | - | 0.0 |
| 0.0 |
|
| 20 | 448 | 207 | - | - | - | 65 | - | - | - | - | - | - | - | - | 0.0 | | O60 | 0.0 | 0 | MIN | 68 | - | - | - | - | 33 | - | - | - | - | - | - | - | - | - | 0.0 |
| 0.0 |
|
| 20 | - | - | - | - | 33 | - | - | - | - | - | - | - | - | - | 0.0 | | H01 | 1 | 0 | TYP | 68 | 77 | 45 | - | - | - | 83 | - | - | - | - | - | - | - | - | 0.0 |
| 25.4 |
|
| 20 | 531 | 310 | - | - | - | 83 | - | - | - | - | - | - | - | - | 0.0 |
*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.
APPLICABLE SPECIFICATIONS:
| Product | Specification |
| Brazing Filler Metal | AWS A5.8 | | Forgings, Die | ASTM B283 |
|