Home > BRONZE > Bronze - Wrought Alloys > C67500

C67500 Manganese Bronze


Atlas carries
C67500 Manganese Bronze in Solid Bar stock. We carry a very large range of sizes and will cut the material to length.
Some of the typical areas that C67500 is used in, is as follows: Valve Bodies, Balls, Valve Stems, Bushings, Aircraft Parts

__________________________________________________________________________________________






Diameters (inch) Part Number
.3125" 6750S-2.5
.3750" 6750S-3
.4375" 6750S-3.5
.5000" 6750S-4
.6250" 6750S-5
.7500" 6750S-6
.8750" 6750S-7
1.000" 6750S-8
1.125" 6750S-9
1.250" 6750S-10
1.375" 6750S-11
1.500" 6750S-12
1.625" 6750S-13
1.750" 6750S-14
2.000" 6750S-16
2.250" 6750S-18
2.500" 6750S-20
2.750" 6750S-22
3.000" 6750S-24
3.250" 6750S-26
3.500" 6750S-28
4.000" 6750S-32
4.500" 6750S-36
5.000" 6750S-40
5.500" 6750S-44
6.000" 6750S-48
7.000" 6750S-56
8.000" 6750S-64
10.00" 6750S-80
11.50" 6750S-92
__________________________________________________________________________________________



TYPICAL USES
Some of the typical areas that C67500 is used in, is as follows: Valve Bodies, Balls, Valve Stems, Bushings, Aircraft Parts



CHEMICAL COMPOSITION

(%max., unless shown as range or min.)
Cu(1) Al Fe Pb Mn Sn Zn
Min./Max. 57.0-60.0 .25 .8-2.0 .20 .05-.50 .50-1.5 Rem.
Nominal 58.5 - 1.4 - .10 1.0 39.0

(1) Cu value includes Ag.
Note: Cu + Sum of Named Elements, 99.5% min.



MECHANICAL PROPERTIES


(measured at room temperature, 68 F (20 C)
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Rod
H01 2 10 TYP 68 72 42 - - 27 77 - - - - - - 44 - 0.0

51

20 496 290 - - 27 77 - - - - - - 303 - 0.0
O60 1 0 TYP 68 65 30 - - 33 65 - - - - - - 42 - 0.0

25.4

20 448 207 - - 33 65 - - - - - - 290 - 0.0
H02 1 20 TYP 68 84 60 - - 19 90 - - - - - - 48 - 0.0

25.4

20 579 414 - - 19 90 - - - - - - 331 - 0.0
H01 1 10 TYP 68 77 45 - - 23 83 - - - - - - 47 - 0.0

25.4

20 531 310 - - 23 83 - - - - - - 324 - 0.0

*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.


APPLICABLE SPECIFICATIONS:

Product Specification
Bar ASTM B138
SAE J463, J461
Bar, Forging ASTM B124
Bolts ASTM F468
Forgings, Die ASTM B283
SAE J463, J461
Nuts ASTM F467
Rod ASTM B138
SAE J463, J461
Rod, Forging ASTM B124
Screws ASTM F468
Shapes ASTM B138
SAE J463, J461
Shapes, Forging ASTM B124
Studs ASTM F468