H02 - Rod / Bar -
Tensile Strength:
Yield Strength:
Elongation:
Rockwell Hardness B Scales:
93 ksi
60 ksi - 0.5% Ext. under load
26%
90
Chemical Composition (%max., unless shown as range or min.)
Need to send a drawing?
We are now accepting the following file types:
Cu(1) Al As Fe Pb Mn Ni(2) Si Sn Zn Min./Max. Rem. 6.3-7.6 .15 .30 .05 .10 .25 1.5-2.2 .20 .50
Nominal 91.2 7.0 - - - - - 1.8 - -
(1) Cu value includes Ag.
(2) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.
Joining Techniques
Soldering
Brazing
Oxyacetylene Welding
Gas Shielded Arc Welded
Coated Metal Arc Welding
Spot Weld
Seam Weld
Butt Weld
Capacity for Being Cold Worked
Capacity for Being Hot Formed
Forgeability Rating
Machinability Rating
Suitability
Not Recommended
Fair
Not Recommended
Fair
Fair
Fair
Fair
Fair
Poor
Excellent
80
60
Mechanical Properties (measured at room temperature, 68 F (20 C)
Fabrication Properties
Typical for 1.5" Rod Cold Worked (15%)
Melting Point - Liquidus
Melting Point - Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Modulus of Rigidity
US Customary
1840 F
1800 F
0.278 lb/in3 at 68 F
7.69
113.0 ohms-cmil/ft @ 68 F
8 %IACS @ 68 F
26.0 Btu · ft/(hr · ft2·oF)at 68F
10.0 ·10-6 per oF (68-572 F)
0.09 Btu/lb/oF at 68 F
16000 ksi
6000 ksi
Physical Properties
Melting Point - Liquidus
Melting Point - Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Modulus of Rigidity
Metric
1004 C
982 C
7.7 gm/cm3 @ 20 C
7.69
18.79 microhm-cm @ 20 C
0.047 MegaSiemens/cm @ 20 C
45.0 W/m · oK at 20 C
18.0 ·10-6 per oC (20-300 C)
377.1 J/kg · oK at 293 K
110000 MPa
41370 MPa
| ||||
| ||||