C64200 Silicon Aluminum Bronze Forgings


Atlas offers
C64200 Silicon Aluminum Bronze Forgings in Plate, Rounds and Rings per ASTM B124 or ASTM B171.

Forgings have distinct advantages over the other methods of Casting (such as Continuous Cast or Sand Castings). Forgings are not only a cost effective process that yields the optimum in performance, but also offer the flexibility of size change. For instance if it becomes necessary to increase a diameter or thickness, open-die forging readily accommodates such a change.

ADVANTAGES
:

  • Reduces the cross-section
  • Improves the metallurgical microstructure
  • Provide directional grain flow
  • Eliminates porosity in Cast ingot





This is a Made to Order product. Tell us what your desired sizes are and we will work up a quote for you. Please indicate if any specifications that must be met.






TYPICAL USES:
Some of the typical areas that C64200 is used in, is as follows: Valve Guides, Automobile Engine, Electrical, Pole Line, Hardware, Fasteners, Bolts, Nuts, Industrial, Valve Components, Valve Bodies, Gears, Valve Stems, Cams, Marine Hardware



CHEMICAL COMPOSITION:

(%max., unless shown as range or min.)
Cu(1) Al As Fe Pb Mn Ni(2) Si Sn Zn
Min./Max. Rem. 6.3-7.6 .09 .30 .05 .10 .25 1.5-2.2 .20 .50
Nominal 91.2 7.0 - - - - - 1.8 - -

(1) Cu value includes Ag.
(2) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.



MECHANICAL PROPERTIES
:

measured at room temperature, 68 F (20 C)
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Rod
M30 0.75 0 TYP 68 75 35 - - 32 77 - - - - - - - - 0.0

19

20 517 241 - - 32 77 - - - - - - - - 0.0
H04 1.5 10 TYP 68 93 60 - - 26 90 - - - - - - - - 0.0

38

20 641 414 - - 26 90 - - - - - - - - 0.0
H04 0.75 15 TYP 68 102 68 - - 22 94 - - - - - - 59 50 0.0

19

20 703 469 - - 22 94 - - - - - - 407 345 0.0
O50 0.75 0 TYP 68 90 55 - - 28 89 - - - - - - - - 0.0

19

20 621 379 - - 28 89 - - - - - - - - 0.0
O50 0.5 0 TYP 68 92 58 - - 22 98 - - - - - - - - 0.0

12.7

20 634 400 - - 22 98 - - - - - - - - 0.0
Forgings
M10 2 0 TYP 68 79 38 - - 30 78 - - - - - - - - 0.0

51

20 545 262 - - 30 78 - - - - - - - - 0.0
Bar
M30 0.75 0 TYP 68 75 35 - - 32 77 - - - - - - - - 0.0

19