Home > ALLOYS > Bronze - Wrought Alloys > C63000 > C63000 Plate

C63000 Nickel Aluminum Plate

Atlas carries C63000 Nickel Aluminum Bronze Plate / Rectangle per ASTM B171, ASME SB171 and is in stock. We also can have it made to Order per your exact requirements. We carry a very large range of thickness and will cut your material to length.

C63000 Aluminum Bronze is an extruded or forged Wrought Alloy that contains Nickel (nominal 5%). As an aluminum bronze, C63000 has an excellent resistance to salt water corrosion and displays exceptional strength and toughness as well. C63000 is typically used where higher mechanical properties are required. It is used in equipment for marine applications, such as: valve stems, high strength bushings, valve guides and seats, gears, cams, ship propellers, as well as propeller nuts and shafts.

Aluminum Bronzes are most commonly used in water applications because of their great resistance to corrosion in a variety of water environments. This makes them preferable to other engineering materials.







Available in the following sizes:

Thickness (inches) Part Number
.2500" 6300P-2
.3750" 6300S-3.5
.5000" 6300S-4
.6250"
6300S-4.5
.7500" 6300S-5
1.000" 6300S-5.5
1.250" 6300S-6
1.500" 6300S-6.5
1.750" 6300S-7
2.000" 6300S-7.5
2.250" 6300S-8
3.000" 6300S-9




TYPICAL USES:

Some of the typical areas that C63000 is used in, is as follows: Valve Seats, Plunger Tips, Condenser Tube for Power Stations and Desalting Units, Shafting, Pump Parts, Cams, Gears, Valve Guides, Aircraft Parts, Pump Shafts, Structural Members, Corrosion Resistant Articles, Hydraulic Bushings for Earth Moving Equipment, Valve Balls, Bushings, Bearings, Heat Exchanger Flanges, Heat Exchanger Headers, Tanks, Welded Piping Systems, Balls



CHEMICAL COMPOSITION:

(%max., unless shown as range or min.)

Cu(1) Al Fe Mn Ni(2) Si Sn Zn
Min./Max. Rem. 9.0-11.0 2.0-4.0 1.5 4.0-5.5 .25 .20 .30
Nominal 82.0 10.0 3.0 - 5.0 - - -

(1) Cu value includes Ag.
(2) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.

C63000 MECHANICAL PROPERTIES

(measured at room temperature, 68 F (20 C)

Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness B
Rockwell
Hardness C
Rockwell
Hardness F
Rockwell
Hardness 30T
Vickens
Hard.
Brinell
Hard. 500
Brinell
Hard. 3000
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Rod
HR50 1

68 118 75 - - -
-
- - - - - - 70
37
0.0

25.4 10
TYP 20 814
517
- - 15 98 - - - - - - 483
255 0.0
HR50 2.01
25.4 TYP 68 100 60 - - -
-
- - - - - - 69 38 0.0

51


20 689 414 - - 18 96 - - - - - - 476 262 0.0
HR50 2.99
25.4 TYP 68 100 60 - - -
-
- - - - - - 65
37
0.0

76


20 689 414 - - 20
96 - - - - - - 448 255 0.0
M30
4.02
25.4 TYP 68 100 60 - - -
-
- - - - - - 6 36 0.0

102

20 689 414 - - 15 96 - - - - - - 427 248 0.0
Bar
TQ50 4.02
-
- 68 100 50 - - -
-
- - - - - - - - 0.0

102
0
TYP
20 689 345
- - 10 96 - - - - - - - - 0.0
HR50 2.01
-
- 68 100 60
- - -
-
- - - - - - - - 0.0

51
10
TYP
20 689 414
- - 15 96 - - - - - - - - 0.0
HR50 1
-
- 68 110 62
- - -
-
- - - - - - - - 0.0

25.4
10
TYP
20 758
427
- - 15 97 - - - - - - - - 0.0
M30
2.99
-
- 68 90
50 - - -
-
- - - - - - - - 0.0

76
0
TYP
20 621 345
- - 15 96 - - - - - - - - 0.0