Products > C61400 Aluminum Bronze
Material:Copper Alloy Number 614  --  Aluminum Bronze
                                                                                                     





Specifications:

     
Applications:



 

Excellent corrosion resistance used in fittings, fasteners, nuts, bolts, tie rods, ball sockets, and heat exchange components, as well as, plastic injection molding dies.


Plate  -  ASTM B171 & B169, ASME SB169, FEDERAL QQ-C-450

Nuts, bolts, corrosion resistant vessels, tanks, components, machine parts, piping systems, heat exchanger tube, marine fasteners, munitions blending chambers    
Click to get a quote:
Plate  -
Tensile Strength:
Yield  Strength:
Elongation:
Rockwell Hardness B Scales:
Minimum 82 ksi    
Minimum 55 ksi - 0.5% Ext. under load        
35% (in 2 inch)       
90
Chemical Composition  (%max., unless shown as range or min.)  
Cu           Al              Fe       Pb   Mn       P      Zn  
Min./Max.  Rem    6.8-8.0   1.5-3.5   .01    1.0     .015   .20
Nominal    91.0     7.0           2.0            -         -         -         - 


Note: Cu + Sum of Named Elements, 99.6% min.
Joining Techniques
Soldering
Brazing
Oxyacetylene Welding
Gas Shielded Arc Welding
Coated Metal Arc Welding
Spot Weld
Seam Weld
Butt Weld
Capacity for Being Cold Worked
Capacity for Being Hot Formed
Machinability Rating
Suitability
Not Recommended
Fair
Not Recommended
Good
Good
Good
Good
Good
Good
Good
20
Mechanical Properties (measured at room temperature, 68 F (20 C)
Fabrication Properties 
Typical for 1" Rod Half Hard (20%) Temper

Melting Point - Liquidus
Melting Point - Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Modulus of Rigidity
US Customary
1915 F
1905 F
0.285 lb/in3 at 68 F
7.89
74.1 ohms-cmil/ft @ 68 F
14 %IACS @ 68 F
39.0 Btu · ft/(hr · ft2·oF)at 68F
9.0 ·10-6 per oF (68-572 F)
0.09 Btu/lb/oF at 68 F
17000 ksi
6400 ksi
Physical Properties  (*Taken from an alloy containing 5% tin and .2% phosphorus. )

Melting Point - Liquidus
Melting Point - Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Modulus of Rigidity
Metric
1046 C
1041 C
7.89 gm/cm3 @ 20 C
7.89
12.32 microhm-cm @ 20 C
0.082 MegaSiemens/cm @ 20 C
67.5 ·10-6 per oC (20-300 C)
16.2 W/m · oK at 20 C
377.1 J/kg · oK at 293 K
117000 MPa
44130 MPa