Atlas carries C51000 Phosphor Bronze, 5% A in Solid Bar stock. We carry a very large range of sizes and will cut the material to length. This alloy possesses a high yield strength and is readily available in most cast products. The typical applications for this alloy are listed below.

C51000 Phosphor Bronze can be readily brazed or soldered and it's capacity for being worked cold worked is good and conforms to specification ASTM B139.






Diameter (inches)
Part Number
0.18755100S-1.5
0.25005100S-2
0.31255100S-2.5
0.37505100S-3
0.43755100S-3.5
0.50005100S-4
0.56255100S-4.5
0.62505100S-5
0.68755100S-5.5
0.75005100S-6
0.81255100S-6.5
0.87505100S-7
0.93755100S-7.5
1.00005100S-8
1.06255100S-8.5
1.12505100S-9
1.18755100S-9.5
1.25005100S-10
1.31255100S-10.5
1.37505100S-11
1.50005100S-12
1.62505100S-13
1.75005100S-14
1.87505100S-15
2.00005100S-16
2.12505100S-17
2.25005100S-18
2.50005100S-20
2.75005100S-22
3.00005100S-24
3.12505100S-25
3.50005100S-28
4.00005100S-32
4.50005100S-36
5.00005100S-40
5.50005100S-44
6.00005100S-48

__________________________________________________________________________________________


Diameter (inches)
Part Number 0.1875 5100S-1.5 0.2500 5100S-2 0.3125 5100S-2.5 0.3750 5100S-3 0.4375 5100S-3.5 0.5000 5100S-4 0.5625 5100S-4.5 0.6250 5100S-5 0.6875 5100S-5.5 0.7500 5100S-6 0.8125 5100S-6.5 0.8750 5100S-7 0.9375 5100S-7.5 1.000 5100S-8 1.0625 5100S-8.5 1.1250 5100S-9 1.1875 5100S-9.5 1.2500 5100S-10 1.3125 5100S-10.5 1.3750 5100S-11 1.5000 5100S-12 1.6250 5100S-13 1.7500 5100S-14 1.8750 5100S-15 2.0000 5100S-16 2.1250 5100S-17 2.2500 5100S-18 2.5000 5100S-20 2.7500 5100S-22 3.0000 5100S-24 3.1250 5100S-25 3.5000 5100S-28 4.0000 5100S-32 4.5000 5100S-36 5.0000 5100S-40 6.0000 5100S-48

TYPICAL USES
Some of the typical areas that C51000 is used in, is as follows:

Clutch disks, cotter pins, diaphragms, fuse clips, fasteners, lock washers, sleeve bushings, springs, switch parts, chemical hardware and welding rods.



CHEMICAL COMPOSITION

(%max., unless shown as range or min.)
Cu Fe Pb P Sn Zn
Min./Max. Rem. .10 .05 .03-.35 4.2-5.8 .30
Nominal 94.8 - - .20 5.0 -

Note: Cu + Sum of Named Elements, 99.5% min.



MECHANICAL PROPERTIES


(measured at room temperature, 68 F (20 C)
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Flat Products
M20 0.0 0 TYP 68 50 - - - - - - - - - - - - - 0.0

0.0

20 345 - - - - - - - - - - - - - 0.0
OS015 0.04 0 TYP 68 53 22 - - 50 34 - 79 - - - - - - 0.0

1

20 365 152 - - 50 34 - 79 - - - - - - 0.0
HR08 0.0 0 TYP 68 103 - 93 - 9 - - - - - - - - - 0.0

0.0

20 710 - 641 - 9 - - - - - - - - - 0.0
O61 0.0 0 SMIN 68 46 - 13 - 47 - - - - - - - - - 0.0

0.0

20 315 - 90 - 47 - - - - - - - - - 0.0
OS035 0.04 0 TYP 68 49 20 - - 58 28 - 75 - - - - - - 0.0

1

20 338 138 - - 58 28 - 75 - - - - - - 0.0
H06 0.04 0 TYP 68 96 - 92 - 3 93 - - 78 - - - - - 0.0

1

20 662 - 634 - 3 93 - - 78 - - - - - 0.0
H01 0.0 0 SMIN 68 49 - 20 - 24 - - - - - - - - - 0.0

0.0

20 340 - 140 - 24 - - - - - - - - - 0.0
H04 0.04 0 TYP 68 84