C11000 ETP Rod / Solid Bar



Atlas carries C11000 Electrolytic Tough Pitch (ETP) Copper Rod or Solid Bar. We carry a very large range of sizes and will cut the material to length.

C11000 Electrolytic Tough Pitch (ETP) Copper is produced by the direct conversion of selected refined cathodes and castings under carefully controlled conditions to prevent contamination of the pure oxygen-free metal during processing. The method of producing OFHC copper ensures extra high grade of metal with a copper content of 99.99%. With so small a content of extraneous elements, the inherent properties of elemental copper are brought forth to a high degree.

This is the most common copper. It is universal for electrical applications. ETP has a minimum conductivity rating of 100% IACS and is required to be 99.9% pure. It has 0.02% to 0.04% oxygen content (typical). Most ETP sold today will meet or exceed the 101% IACS specification. As with OF copper, silver (Ag) content is counted as copper (Cu) for purity purposes.
















Diameter (in)
Part Number
0.3750 1100S-3
0.6250 1100S-5
1.1250 1100S-9
1.2500 1100S-10
1.3750 1100S-11



TYPICAL USES
Some of the typical areas that C11000 is used in, is as follows:

Building Fronts, Gutters, Skylight Frames, Roofing, Flashing, Downspouts, Spouting
Pressure Vessels, Chemical Process Equipment, Chlorine Cells, Chimney Cap Screens, Heat Exchangers, Printing Rolls, Anodes, Rotating Bands, Kettles, Pans, Vats, Road Bed Expansion Plates



CHEMICAL COMPOSITION

(%max., unless shown as range or min.)
NOTE: Information courtesy copper.org

Cu(1) O
Min./Max. 99.90 min -
Nominal - .04

(1) Cu value includes Ag.
Note: This is a high conductivity copper which has, in the annealed condition a minimum concuctivity of 100% IACS except for Alloy C10100 which has a minimum conductivity of 101% IACS.
Note: Oxygen and trace elements may vary depending on the process.



MECHANICAL PROPERTIES


(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy copper.org
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Flat Products
H02 0.04 0 TYP 68 42 36 - - 14 40 - 84 50 - - - 26 13 0.0

1

20 290 248 - - 14 40 - 84 50 - - - 179 90 0.0
M20 0.025 0 TYP 68 32 10 - - 50 - - 40 - - - - 22 - 0.0

0.64

20 221 69 - - 50 - - 40 - - - - 152 - 0.0
Rod
M20 1 0 TYP 68 32 10 - - 55 - - 40 - - - - 22 - 0.0

25.4

20 221 69 - - 55 - - 40 - - - - 152 - 0.0
Shapes
M30 0.5 0 TYP 68 32 10 - - 50 - - 40 - - - - 22 - 0.0

12.7

20 221 69 - - 50 - - 40 - - - - 152 - 0.0
M20 0.5 0 TYP 68 32 10 - - 50 - - 40 - - - - 22 - 0.0

12.7

20 221 69 - - 50 - - 40 - - - - 152 - 0.0
Flat Products
H04 0.04 0 TYP 68 50 45 - - 6 50 - 90 57 - - - 28 - 0.0

1

20 345 310 - - 6 50 - 90 57 - - - 193 - 0.0
Rod
H04 0.25 40 TYP 68 55 50 - - 10 60 - 94 - - - - 29 - 0.0

6.35

20 379 345 - - 10 60 - 94 - - - - 200 - 0.0
Flat Products
H08 0.04 0 TYP 68 55 50 - - 4 60 - 94