C10200 Copper Tubing



Atlas carries
C10200 Oxygen Free (OF) Copper in Tubing. We carry a very large range of sizes and will cut the material to length.

C10200 Oxygen Free (OF) Copper is produced by the direct conversion of selected refined cathodes and castings under carefully controlled conditions to prevent contamination of the pure oxygen-free metal during processing. The method of producing OFHC copper ensures extra high grade of metal with a copper content of 99.99%. With so small a content of extraneous elements, the inherent properties of elemental copper are brought forth to a high degree.

While OF is considered oxygen-free, its conductivity rating is no better than the more common ETP or C11000 grade copper. It has a 0.001% oxygen content, 99.95% purity and minimum 100% IACS conductivity. For the purposes of purity percentage, silver (Ag) content is counted as copper (Cu).


___________________________________________________________________________________________






OD (inches)
Wall (inches)Part Number
0.5000.1251020T-4-1
0.6250.1251020T-5-1
0.7500.0321020T-6-0.256
0.7500.0621020T-6-0.496
0.8750.0321020T-7-0.256
0.8750.0651020T-7-0.52




TYPICAL USES

Some of the typical areas that C10200 is used in, is as follows: Microwave Tubes, Copper to Glass Seals in Electronic Appliances, Wave Guides, Bus Conductors, Busbars, Klystrons, Coaxial Cables, Electrical Conductors, Lead In Wire, Transistor Component, Billet Mold Tube, Coaxial Tube, Extrusion Cans for Powder Metallurgy, Vacuum Seals, Tubing, LP Gas Service, Tubing, Medical Gas- Oxygen



CHEMICAL COMPOSITION

(%max., unless shown as range or min.)
NOTE: Information courtesy
copper.org

Cu(1) O
Min./Max. 99.95 min .0010
Nominal - -

(1) Cu value includes Ag.
Note: This is a high conductivity copper which has, in the annealed condition a minimum concuctivity of 100% IACS except for Alloy C10100 which has a minimum conductivity of 101% IACS.



MECHANICAL PROPERTIES


(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy copper.org
Temper Section
Size
Cold
Work
Typ/
Min
Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Flat Products
H02 0.04 0 TYP 68 42 36 - - 14 40 - 84 50 - - - 26 13 0.0

1

20 290 248 - - 14 40 - 84 50 - - - 179 90 0.0
M20 0.25 0 TYP 68 32 10 - - 50 - - 40 - - - - 22 - 0.0

6.35

20 221 69 - - 50 - - 40 - - - - 152 - 0.0
H04 0.25 0 TYP 68 50 45 - - 12 50 - 90 - - - - 28 - 0.0

6.35

20 345 310 - - 12 50 - 90 - - - - 193 - 0.0
Rod
M20 1 0 TYP 68 32 10 - - 55 - - 40 - - - - 22 - 0.0

25.4

20 221 69 - - 55 - - 40 - - - - 152 - 0.0
Shapes
M30 0.5 0 TYP 68 32 10 - - 50 - - 40 - - - - 22 - 0.0

12.7

20 221 69 - - 50 - - 40 - - - - 152 - 0.0
M20 0.5 0 TYP 68 32 10 - - 50 - - 40 - - - - 22 - 0.0

12.7

20 221 69 - - 50 - - 40 - - - - 152 - 0.0
Flat Products
H04 0.04 0 TYP 68 50 45 - - 6 50 - 90 57 - - - 28 13 0.0

1

20 345 310 - - 6 50 - 90 57 - - - 193 90 0.0
Rod
H04 0.25 40